All Products
-
Silicone Coated Fiberglass Fabric
-
Fire Resistant Fiberglass Fabric
-
High Temperature Fiberglass Cloth
-
PU Coated Fiberglass Fabric
-
PTFE Coated Fiberglass Fabric
-
Aluminum Foil Fiberglass Cloth
-
Heat Resistant Fabrics
-
Welding Blanket Roll
-
Fire Curtain Fabric
-
Thermal Insulation Fabric
-
Industrial Fire Blanket Roll
-
Fabric Expansion Joint Cloth
-
Heat Reflective Fabric
-
Woven Fiberglass Cloth
-
Chemical Resistant Fabric
-
Fiberglass Tape Rope Sleeve
-
Fire Pit Mat
-
Jacky HuangThey are a trust partner truly. They deliver goods fast with satisfying quality.And they are professional in high temperature textiles, always contribute for different projects. -
MS. HandeWe have been working with Suntex for over 10 years, they keep quality stable always. They treat every single request of us seriously. It's happy to work together with them anyway.
800 C High Temperature Thermal Insulation Fabric For Making Removable Jacket And Covers
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Thickness | 1.4 Mm Thickness | Weave Tape | Panama Weave |
|---|---|---|---|
| Weight | 1220 G/sqm | Color | Silver Grey |
| Width | 1.5 M | Roll Length | 50 M |
| Technology | Stainless Steel Wire Inserted | Coating | Calcium Silicate |
| Application | Insulation Covers / Insulation Blanket | ||
| High Light | silicone impregnated fiberglass fabric,heat reflective fabric |
||
Product Description
Stainless Steel Wire Inserted Woven Fiberglass Fabric With Calcium Silicate Coating
Description:
stainless steel wire inserted woven texturized fiberglass fabric is an engineering material, fiberglass fabric has the excellent merit such as anti-burns, anti-corrosion, stable-size, heat-isolation, minimum elongated shrinkage, high intensity; fiberglass fabric has already covered many domains such as electric appliance, electronic, transportation, chemical engineering, architectural engineering, heat insulation, sound absorption, fire prevention and environmental protection, etc.
TGF1200S-CS213-5030 is a stainless steel wire inserted woven texturized fiberglass fabric coated with a formulated inorganic solution which provides high temperature and abrasion resistance properties for the manufacturer of gaskets, flexible expansion joints, removable jackets and other types of fire control systems. This style withstands temperature extremes of up to 800 0C, no significant deterioration in flexibility or strength, without smoke/fumes release when catches fire.
Date sheet:
| BASE FABRIC | Base fabric style No. TGF1200S | |||
| (Metric) | (English) | Test methods | ||
| Weave | Panama | Panama | ||
| Yarn | ||||
| Warp |
ET9 1250 tex S.S 316# wire |
ETG 4.0 S.S 316# wire |
||
| Weft |
ET9 770 tex S.S 316# wire |
ETG 6.5 S.S 316# wire |
||
| Construction | ||||
| Warp | 6 ± 0.6 ends /cm | 15 ± 2 ends/inch | ASTM D 3775-96 | |
| Weft | 5.5 ± 0.5 picks /cm | 14 ± 2 picks/inch | ASTM D 3775-96 | |
| COATED FABRIC | Coating style No. CS213-5030 | |||
| Coating | Formulated inorganic solutions coated on both sides | |||
| Weight | 1220 ± 50 g/m2 | 36 ± 1.47 oz/yd2 | ASTM D3776-96 | |
| Thickness | 1.4 ± 0.07 mm | 0.055 ± 0.003 inch | ASTM D1777-96 | |
| Color | Grey | |||
| Temp resistance |
7500C for the coating 8000C for the base fabric |
|||
Application:
High temperature welding blanket
Removable insulation mattress, jacket & pad
Fire doors/smoke curtain
Flexible expansion joints & compensators
Advantages:
Excellent anti abrasion property
Easy to be cut, sewn and fabricated
14 years experience Chinese supplier
3rd party certificate insulation verified
High temperature esiatent up to 800C