Silica Material Silicone Coated Fabric Resistant High Temperature Up To 1000 C Degree
Silicone coated fiberglass fabric is a woven material available in various sizes to allow custom strength, thickness, and weight in projects. Fiberglass cloth provides great strength and durability when layered with a resin to form a hardened composite.
|Basic fabric||(Metric)||(English)||Test methods|
|Weave||8 H Satin||8 H Satin|
|Warp||19 ± 1 ends/cm||48 ± 3 ends/inch||ASTM D 3775-96|
|Weft||14 ± 1 picks/cm||33 ± 3 picks/inch||ASTM D 3775-96|
|Weight||600 ± 150 g/m2||18 ± 4.4 oz/yd2||ASTM D3776-96|
|Thickness||0.65 ± 0.08 mm||0.025± 0.003 inch||ASTM D1777-96|
|Standard width||91.4 ± 1 cm||36 ± 0.39 inch||ASTM D3776-96|
|100.0± 1 cm||39± 0.39 inch|
|Warp||800 N/25mm||ASTM D5034-95|
|Weft||500 N/25mm||ASTM D5034-95|
|COATED FABRIC||Coating style No. SI254-1160|
|Fiberglass Cloth Roll Coating||Silicon coated ,2 sides|
|Weight||850 ± 50 g/m2||25 ± 1.50 oz/yd2|
|Thickness||0.8 ± 0.1 mm||0.051 ± 0.004 inch|
Working temperature for basic fabric at 10000C
Working temperature for silicone coating at 2600C
1. Electrical insulation:It have high electrical insulation grade ,can bead high voltage,can be made of insulation cloth,sleeve etc.
2. Non-metallic compensator:Silicone cloth can be used as flexible connector of pepeline,silicone rubber coated glass fiber membrane structure material as base material of the flexible expansion joint, it can solve the damage of thermal expansion cold shrink to pipe,silicone cloth has high temperature resistance,anti-corrosion ,aging resistance,good elasticity and flexibility ,can be widely used in petroleum,chemical,cement,energy and other fields.
3. Anti-corrosion:Silicone rubber coated glass fiber cloth can be used as internal and external anticorrosive coating for pipe,Excellent corrosion resistance,high strength ,it is an ideal anticorrosion material.
4.Other fields:silicone rubber coated glass fiber membrane structure material can be can be used in building sealing materials,high temperature anticorrosion conveyor belt,packaging materials and other fields.
Easy to cut and sewing
Short lead time (5-15 days)
P&D department to ensure the quality
Contact Person: admin